Influence of antimony addition in the directionally solidified hypoeutectic Sn-52wt.%Bi alloy: thermal, microstructural parameters and mechanical resistance

PALAVRAS-CHAVES:

Solidification; Thermal Parameters; Sn-Bi-Sb alloys; Microstructure; Tensile Mechanical properties.

PÁGINAS: 95
GRANDE ÁREA: Engenharias
ÁREA: Engenharia de Materiais e Metalúrgica
RESUMO:

The search for sustainable and less toxic materials is a global trend and should draw even more attention in the coming years due to the new and current restrictions/directives of environmental agencies. Lead-free solder alloys used in the electronics industry are examples of this scenario. In this context the present investigation aims to establish correlations between the solidification thermal parameters (cooling rate-ṪL and growth rate-VL) and microstructural parameters (primary-λ1, secondary-λ2 and tertiary-λ3 dendritic; and fine-λF and coarse-λC eutectic spacings) for the directionally solidified (DS) Sn-52wt.%Bi-1wt.%Sb and Sn-52wt.%Bi-3wt.%Sb alloys under transient heat flow conditions. A dendritic array was identified for the Sn-Bi-Sb alloys formed by a Sn-rich matrix with Bi precipitates at its core, surrounded by lamellar eutectic structures (Sn-rich+Bi-rich), Bi trifolis and fishbone-like eutectic. The significant fraction of eutectic mixture (Sn-rich+Bi-rich) in the Sn-Bi-Sb alloys induced the -1/4 and -1/2 exponents, proposed by Jackson and Hunt for eutectics, characterize the evolutions of λ1, λ3 and λ2, as a function of ṪL and VL, respectively. These exponents also characterized evolutions of λF and λC against ṪL and VL for the modified alloy containing 1wt.%Sb. Hall-Petch type correlations for Sn-Bi-Sb alloys displayed that additions of 1wt.% and 3wt.%Sb have beneficial effects on the ultimate tensile strength-σu and the yield tensile strength-σy, but does not affect ductility (elongation to fracture-δ)

MEMBROS DA BANCA:
Presidente - 2345599 - BISMARCK LUIZ SILVA
Externo ao Programa - 1652765 - MAURÍCIO MHIRDAUI PERES
Externo ao Programa - 2414250 - MEYSAM MASHHADIKARIMI
Interno - 1350249 - RUBENS MARIBONDO DO NASCIMENTO