Banca de QUALIFICAÇÃO: ANDERSON COSTA MARQUES

Uma banca de QUALIFICAÇÃO de MESTRADO foi cadastrada pelo programa.
STUDENT : ANDERSON COSTA MARQUES
DATE: 31/10/2024
TIME: 09:30
LOCAL: meet.google.com/byk-gstw-ose
TITLE:

Production of High-Entropy Carbide (TiVTaNbW)C via High-Energy Ball Milling

KEY WORDS:

High-Entropy Carbide; (TiVTaNbW)C; High-Energy Ball Milling; SPS.

PAGES: 100
BIG AREA: Engenharias
AREA: Engenharia de Materiais e Metalúrgica
SUBÁREA: Metalurgia de Transformação
SPECIALTY: Metalurgia de Pó
SUMMARY:

High-entropy alloy-based ceramic carbides represent a new class of materials that has garnered significant interest within the scientific community and industries such as aerospace, thermal spray coatings, high-temperature molds and dies, cutting tools, and radiation-resistant shields. Various carbide compositions are produced using different processing methods. This study aims to obtain equimolar High-Entropy Carbide (HEC), (TiVTaNbW)C, via High-Energy Ball Milling (HEBM), using metallic precursor powders. HEBM occurs in two stages: the first involves the formation of the high-entropy alloy (TiVTaNbW), with milling cycles of 6, 12, and 18 hours; the second focuses on obtaining the HEC, analyzed at 6 and 12 hours, both at 500 RPM. The carbide’s properties were analyzed using X-Ray Diffraction (XRD), Scanning Electron Microscopy (SEM), Fourier Transform Infrared Spectroscopy (FTIR), Spark Plasma Sintering (SPS), Vickers Hardness, Confocal Microscopy, and Pin-on-Disk tribological tests. XRD revealed characteristic carbide peaks, while SEM showed carbide regions and the surface element distribution. FTIR indicated typical metal-carbon bonding bands, and SPS improved the material’s properties, reaching a Vickers hardness of 16.24 ± 2.01 GPa and a KIC value of 6.83 ± 0.73 MPa√m, as obtained by confocal analysis. The Pin-on-Disk test recorded a wear rate of 285.17 μm and a friction coefficient of 0.46. The results confirm that obtaining (TiVTaNbW)C via High-Energy Ball Milling is a promising process with potential applications in industries requiring high wear resistance, corrosion resistance, high hardness, thermal stability, and fracture toughness.

COMMITTEE MEMBERS:
Interno - 1300987 - CARLOS ALBERTO PASKOCIMAS
Externo à Instituição - MARCELLO FILGUEIRA
Presidente - 2414250 - MEYSAM MASHHADIKARIMI
Interno - 1350249 - RUBENS MARIBONDO DO NASCIMENTO
Interno - ***.121.804-** - UILAME UMBELINO GOMES - UFRN